NORPOL FI-177-10 is a low exotherm, light-weight sandwich adhesive, based on a high quality ISO/NPG resin. NORPOL FI-177-10 is accelerated and changes colour from light blue to white shortly after the admixing of peroxide.
•Recommended peroxide dosage: 1.5% low exothermic Peroxide (NORPOL PEROXIDE 19)
•Recommended application temperature interval 18-23 ºC
VARIOUS PROPERTIES
NORPOL FI-177-10 is mainly used to bond single core material sheets together and for bonding core material to GRP laminates.
NORPOL FI-177-10 is formulated for use in vacuum bagging.
The bonding paste should be stored at 18-25 ºC .If the product have a temperature <18 ºC (which is no problem as to product quality) it should be heated to 18-25 ºC before use. See storage and handling document of NORPOL products.
AVAILABILITY
Europe / Middle East / Africa
|
|
NORPOL FI-170 is a multi-purpose bonding paste based on special polyester resins combined with selected fillers and additives.
NORPOL FI-170 is pre-accelerated and has a white colour. NORPOL FI-170 changes colour from bluish white to white in <5min. after the admixing of peroxide.
•Recommended peroxide dosage: 1.5% MEK Peroxide (NORPOL Peroxide 1)
•Recommended application temperature interval 18-23 ºC
•Sag/flow: Will not sag provided a maximum thickness of 15 mm is observed. Not horizontally self-flowing.
Applicable as a general purpose bonding paste.
VARIOUS PROPERTIES
Suitable surfaces: Glass-fibre reinforced products and cellular plastics.
Workability: Hard to grind.
The bonding paste should be stored at 18-25 ºC. If the product is below a temperature of 18 ºC (which does not affect product quality) it should be heated to 18-25 ºC before use. See storage and handling document of NORPOL products.
AVAILABILITY
Europe / Middle East / Africa
|
|
The GRAVICOL® range of bonding pastes are designed for the assembly and bonding of glass reinforced plastic moldings. All of the bonding pastes in the range are pre-accelerated and require only the addition of a
standard MEKP catalyst. The pastes can be used for bonding two parts, insert panels, core materials. They can also be used for cavity filling and as an aid to lamination to help reduce the chance of air voids. When designing the bonding pastes there are several key areas we look at and control to
suit the numerous application areas of the pastes : - Gel/Cure Times - Low Shrinkage Levels - Application Methods - Mechanical Properties
|
|
| ... products without technical information |
| |
NORPOL FI-177-10 is a low exotherm, light-weight sandwich adhesive, based on a high quality ISO/NPG resin. NORPOL FI-177-10 is accelerated and changes colour from light blue to white shortly after the admixing of peroxide.
•Recommended peroxide dosage: 1.5% low exothermic Peroxide (NORPOL PEROXIDE 19)
•Recommended application temperature interval 18-23 ºC
VARIOUS PROPERTIES
NORPOL FI-177-10 is mainly used to bond single core material sheets together and for bonding core material to GRP laminates.
NORPOL FI-177-10 is formulated for use in vacuum bagging.
The bonding paste should be stored at 18-25 ºC .If the product have a temperature <18 ºC (which is no problem as to product quality) it should be heated to 18-25 ºC before use. See storage and handling document of NORPOL products.
AVAILABILITY
Europe / Middle East / Africa
|
|
NORPOL FI-170 is a multi-purpose bonding paste based on special polyester resins combined with selected fillers and additives.
NORPOL FI-170 is pre-accelerated and has a white colour. NORPOL FI-170 changes colour from bluish white to white in <5min. after the admixing of peroxide.
•Recommended peroxide dosage: 1.5% MEK Peroxide (NORPOL Peroxide 1)
•Recommended application temperature interval 18-23 ºC
•Sag/flow: Will not sag provided a maximum thickness of 15 mm is observed. Not horizontally self-flowing.
Applicable as a general purpose bonding paste.
VARIOUS PROPERTIES
Suitable surfaces: Glass-fibre reinforced products and cellular plastics.
Workability: Hard to grind.
The bonding paste should be stored at 18-25 ºC. If the product is below a temperature of 18 ºC (which does not affect product quality) it should be heated to 18-25 ºC before use. See storage and handling document of NORPOL products.
AVAILABILITY
Europe / Middle East / Africa
|
|
The GRAVICOL® range of bonding pastes are designed for the assembly and bonding of glass reinforced plastic moldings. All of the bonding pastes in the range are pre-accelerated and require only the addition of a
standard MEKP catalyst. The pastes can be used for bonding two parts, insert panels, core materials. They can also be used for cavity filling and as an aid to lamination to help reduce the chance of air voids. When designing the bonding pastes there are several key areas we look at and control to
suit the numerous application areas of the pastes : - Gel/Cure Times - Low Shrinkage Levels - Application Methods - Mechanical Properties
|
|
| ... products without technical information |
| |
- Label material for cables, wires, cabinets and components.
- For PARTEX holder systems PT+, PTZ , PM and PS.
- Easy to separate in rigid polyester foil, specially pre-processed for printing.
- Halogen free.
- Print-out by matrix or laser printer.
- Fast, convenient marking on site with PARTEX software WINSIGT for Windows.
- A low cost 2-component solution for marking before and after connection of wires and cables.
|
|
Tapes with a polyester film backing and different adhesives
Polyester film backing imparts excellent chemical and thermal stability.
|
|
|
|