Crystal Structure:
Trigonal,Space Group R3c
Orthorhombic,Point Group mm²
Orthorhombic,Point Group mm²
Trigonal,Space Group R3c
Transparency Range:
189-3500nm
350-4500nm
160-2600nm
420-5200nm
Cell Parameters:
A=b=12.532 Å
C=12.717 Å
A=6.404 Å
B=10.616 Å
C=12.814 Å
A=8.44731Å
B=7.3788 Å
C=5.1395 Å
a=0.515Å
c=13.863Å
Melting Point:
1095+/-5℃
1172℃ Incongruent
834℃
1255+/-5℃
Curie Point:
925+/-5℃
936℃
5
1140+/-5℃
Optical Homogeneity:
△n=10-6/cm
△n=10-6/cm
△n=10-6/cm
△n=5*10-5/cm
Mohs Hardness:
4.5
5
6
5
Density:
3.85g/cm³
3.01g/cm³
2.47g/cm³
4.64g/cm³
Thermal Conductivity:
ˆC,0.012W/m/k
‖C,0.016W/m/k
0.03 W/m/k
0.035 W/m/k
0.046 W/m/k
Phase-matchable SHG Range:
205-1750nm
1000-2000nm
800-2000nm
1100-3000nm
Absorption Coefficient:
<0.1%/cm@1064nm
<1%/cm@1064nm and 532nm
<=1%/cm@1064nm
<0.1%/cm@1064nm
NLO coefficients:
d21=2.2pm/V
d31=0.08pm/V
d22=2.2pm/V
d31=1.95pm/V
d32=3.90pm/V
d33=15.3pm/V
d24=3.90pm/V
d15=1.95pm/V
d21=0.67pm/V
d22=0.04pm/V
d23=0.85pm/V
d34=0.85pm/V
d16=0.67pm/
d21=d22=d16=2.6pm/V
d31=d32=d24=4.6pm/V
d33=25.6 pm/V
Damage Threshold@1064nm:
12.9J/cm² 9.9GW/ cm²
6.0J/cm² 4.6GW/ cm²
24.6J/cm² 18.9GW/ cm²
200GW/ cm²
Refractive Indices@1064nm@532nm:
Ne=1.5425
No=1.6551
Ne=1.5555
No=1.6749
Nx=1.73991
Ny=1.74802
Nz=1.82956
Nx=1.77903
Ny=1.79002
Nz=1.88628
Nx=1.56447
Ny=1.59050
Nz=1.60538
Nx=1.57842
Ny=1.60650
Nz=1.6215
Ne=2.23216
No=2.15600
Ne=2.32309
No=2.23415