Packaging film ZCR01

for food packagingshrinkpolyolefin

Description
This polyolefin shrink film ZCR01 contains 30% post-consumer recycled polyethylene (PCR). It is manufactured using the same production process as ZDF01 and offers comparable mechanical and sealing properties while improving recycled content. The film provides reliable heat sealing, high shrinkage and compatibility with a wide range of packaging machines.

Certification
The film is certified to GRS 4.0 (Global Recycle Standard).

Thickness
Available gauges: 15 µm, 19 µm, 25 µm, 30 µm.

Application areas

• Food packaging
• Vegetables
• Beverages
• Electronic products
• Tea
• Dairy (milk)
• Handicrafts and consumer goods

Performance — Advantages

• Contains >30% post-consumer recycled material (PCR) to reduce virgin resin usage.
• Performance comparable to conventional POF shrink films (mechanical strength, sealing).
• High transparency and high shrinkage for tight, clear packages.
• Good heat-seal properties and adaptability to various packaging machines.
• Printable surface; multiple styles and printing options supported.

Performance — Parameters

• Introduction: Post Consumer Recycling: 30% recycled post-consumer polyethylene (RM0193).
• Gauge (thickness): 15 / 19 / 25 / 30 µm.
• Tensile Strength (MD / TD) (ASTM D882): 115 / 110 / 90 / 88 N/mm² (MD) ; 110 / 105 / 85 / 80 N/mm² (TD).
• Elongation at break (MD / TD): 105 / 110 / 105 / 100 % (MD) ; 100 / 105 / 95 / 90 % (TD).
• Tear Strength MD / TD (D1922, 400 g): MD 10.5 / 13.5 / 16.5 / 20.5 gf ; TD 9.8 / 12.5 / 16.5 / 22.5 gf.
• Seal Strength — Hot Wire Seal (MD / TD) (F88): MD 0.85 / 0.95 / 1.15 / 1.35 N/mm ; TD 1.05 / 1.15 / 1.25 / 1.55 N/mm.
• COF film-to-film (Static / Dynamic, D1894): 0.20 / 0.18 / 0.22 / 0.23.
• Optics — Haze (D1003): 3.5 / 3.8 / 4.0 / 4.3 ; Clarity (D1746): 93.0 / 92.0 / 91.0 / 90.0 ; Gloss @45° (D2457): 85.0 / 82.0 / 80.0 / 81.0.
• Barrier — OTR (cc/m²/day, D3985): 9200 / 8200 / 5600 / 4200 ; WVTR (g/m²/day, F1249): 25.9 / 17.2 / 14.5 / 11.2.
• Shrinkage properties (Free Shrinkage % @100°C, D2732): MD 17 / 32 / 54 / 68 % ; TD 26 / 44 / 59 / 69 % (values correspond to 15 / 19 / 25 / 30 µm).
• Shrink Tension @100°C (D2838): MD 1.65 / 2.55 / 2.70 / 2.45 MPa ; TD 2.35 / 3.20 / 3.45 / 3.10 MPa.

Disclaimer
The information provided is based on internal testing and is for reference only. The company assumes no liability for the use of this information.