Lead-free soldering wire S01X7Ca-72M

heating elementcopper-coated steel

0.1%Ag for Longer-lasting Iron Tips Inhibits erosion of Fe plating Co added to S01X7Ca-72M forms a barrier layer at the iron tip surface, which inhibits erosion of the tip. S01X7Ca-72M significantly reduces wear of iron tips compared to regular lead-free solder. Prevents bridging in slide soldering 72M series contain new activators for improved wettability and new resin composition for better flux coverage. They can prevent bridging even at defect prone conditions such as low iron tip temperature or fast sliding speed. ■Image of slide soldering Ultimate cost reduction by flux-cored solder Ag content of S01X7Ca-72M is 0.1%. Absolutely low Ag content achieves significant cost reduction, assisting realization of ultimate cost reduction along with its erosion inhibition effect. Product Performance Table Product Name S01X7Ca-72M Product Category Flux Cored Solder Wire Melting Point(℃) 217-227 Flux Content(%) 3.2 Halide content(%) < 0.01 Flux Type ROL0 (IPC J-STD-004) Diameter(mm φ) 0.3, 0.5, 0.6, 0.8, 1.0 ,1.2