Corrosion protection coating service Inoxplate

wear-resistantprotectivehydro-oleophobic

Short description
It offers a top range appearance, fingerprint protection and easy surface cleaning, improving corrosion resistance of uncoated stainless steel.

General

• It maintains the same decorative look as the material used as substrate.
• Anti-fingerprint material, highly resistant to scratching.
• Pressurised-water cleaning test for 1 hour, 100 bars at 20 cm = no delamination or separations.
• Very good resistance to stains and household cleaning products, thus protecting the stainless steel from premature ageing.
• Excellent resistance to dampness.
• Maximum use temperature 110 °C. Inert material, food safe.
• Great folding flexibility, but cannot be welded.

Product behaviour
DESCRIPTION | TESTING STANDARD | UNIT | RESULT | OBSERVATIONS
Total coating thickness | EN 13523-1 / ASTM D1005 | μ | 18 |
Specular Gloss (Gardner 60º) | EN 13523-2 / ASTM D523 | % | > 90 | depending on finish
Pencil hardness | EN 13523-4 / ASTM D3363 | | > 4H |
Resistance to rapid deformation | EN 13523-5 / ASTM D2794 | joules | 18 | without detachment
Adherence after Erichsen cupping | EN 13523-6 / ASTM E643 | mm | 8 | without detachment
T Bending | EN 13523-7 / ASTM D522 | | 0T | without cracking or separation
Resistance to salt spray | EN 13523-8 / ASTM B117 | hours | 500 | 5mm max. detachment
Resistance to accelerated Xenotest ageing test | EN 13523-10 / ASTM D6695 | hours | > 1000 | ΔE < 1
Resistance to MEC friction test | EN 13523-11 / ASTM D5402 | DF | > 150 | without change
Stain resistant (strawberry, orange, butter, fried tomato, mustard, lipstick, oil, milk, coffee, tea, chocolate, and soap) | EN 13523-18 / ASTM D1308 | | stain free | after 24 hours

Caractéristiques / spécifications techniques

• Total coating thickness: 18 μm.
• Specular gloss (Gardner 60º): > 90% (depending on finish).
• Pencil hardness: > 4H.
• Resistance to rapid deformation: 18 J without detachment.
• Adherence after Erichsen cupping: 8 mm without detachment.
• T Bending: 0T without cracking or separation.
• Salt spray resistance: 500 hours (max. 5 mm detachment).
• Xenotest ageing: > 1000 hours (ΔE < 1).
• MEC friction test: DF > 150 without change.
• Stain resistance: stain free after 24 hours for common stains (listed above).
• Pressurised-water cleaning: 1 hour at 100 bars, 20 cm — no delamination or separations.
• Maximum use temperature: 110 °C. Inert material and food safe.
• Great folding flexibility; cannot be welded.
• Typical industries: Automotive; Commercial Cooling; Domestic Appliances; Elevators.